Multiple Cracking of Metallized Polyimide Kapton Films

Authors

  • S. L. Bazhenov Department of Solid State Physics, Moscow State Pedagogical University, 29 M. Pirogovskaya street, Moscow, Russia
  • I. N. Nasrullaev Department of Solid State Physics, Moscow State Pedagogical University, 29 M. Pirogovskaya street, Moscow, Russia
  • I. V. Razumovskaya Department of Solid State Physics, Moscow State Pedagogical University, 29 M. Pirogovskaya street, Moscow, Russia
  • Saule K. Kudaikulova Institute of Chemical Sciences, 106 Walikhanov Street, 480100, Almaty, Kazakhstan
  • B. A. Zhubanov Institute of Chemical Sciences, 106 Walikhanov Street, 480100, Almaty, Kazakhstan
  • Marc J.M. Abadie Laboratory of Polymer Science & Advance Organic Materials, Montpellier University 2, S.T.L., Place Eugène Bataillon, 34095 Montpellier Cedex 05, France

DOI:

https://doi.org/10.18321/ectj332

Abstract

Mechanical behaviour of metallized polyimide Kapton films was studied. The adhesion of metallized films to Kapton films is approximately hundred-folds higher than that of coatings made by usual sputter deposition of a metal on a polymer substrate. Multiple cracking of a metallized film was observed. Cracks of two different scale levels are observed. The cracks of the first type (microcracks) are short with 1-2 µm length. The cracks of the second type are much longer and have length of several hundreds microns. The cracks of this type appear at higher strains as compared with the shorter ones. In thinner 7-µm-thick samples long cracks were not observed.

References

(1). D.R. Wheeler, H. Osaki, ACS Symposium Series, 440: 500 (1990).

(2). Y. Leterrier, L. Boogh, J. Andersons, J.-A.E. Manson, J.Polym.Science, part B, Physics, 35: 1449 (1997).

(3). Y. Leterrier, L. Boogh, J. Andersons, J.-A.E. Manson, J.Polym.Science, part B, Physics, 35: 1463 (1997).

(4). S.L. Bazhenov, I.V. Chernov, A.L. Volynskii, and N.F. Bakeev, Doklady of Academy of Science, V. 356: 199 (1997).

(5). A.L.Volynskii, S.L. Bazhenov, O.V.Lebedeva, A.N.Ozerin, and N.F.Bakeev, Vysokomol. Soedin., Ser. A, 39: 1827 (1997).

(6). F. Faupel, C.H. Yang, S.T. Chen, and P.S. Ho, J. Appl. Phys., 26: 1911 (1989).

(7). A. Kelly, W.R. Tyson, J.Mech.Phys.Solids, 13: 329 (1965).

(8). A.L. Volynskii, O.V. Lebedeva, S.L. Bazhenov and N.F. Bakeev, Vysokomol.Soedin., Ser.A, 42: 438 (2000).

(9). S. Bazhenov Composites, 26:125 (1995).

(10). A.L. Volinskii, S. Bazhenov, O.V. Lebedeva, A.N. Ozerin, N.F. Bakeev, J. Appl. Polymer Science, 72: 1267 (1999).

Downloads

Published

2004-03-25

How to Cite

Bazhenov, S. L., Nasrullaev, I. N., Razumovskaya, I. V., Kudaikulova, S. K., Zhubanov, B. A., & Abadie, M. J. (2004). Multiple Cracking of Metallized Polyimide Kapton Films. Eurasian Chemico-Technological Journal, 6(1), 41–44. https://doi.org/10.18321/ectj332

Issue

Section

Articles