Evaluation of Synthetic Conditions for H3PO4 Chemically Activated Rice Husk and Preparation of Honeycomb Monoliths

Authors

  • J. M. Jandosov Al-Faraby Kazakh National University, 71, al-Farabi av., 050038, Almaty, Kazakhstan
  • N. V. Shikina Boreskov Institute of Catalysis, 5, Pr. Akad. Lavrentieva, 630090, Novosibirsk, Russia
  • M. A. Bijsenbayev Al-Faraby Kazakh National University, 71, al-Farabi av., 050038, Almaty, Kazakhstan
  • M. E. Shamalov Al-Faraby Kazakh National University, 71, al-Farabi av., 050038, Almaty, Kazakhstan
  • Z. R. Ismagilov Boreskov Institute of Catalysis, 5, Pr. Akad. Lavrentieva, 630090, Novosibirsk, Russia
  • Z. A. Mansurov Al-Faraby Kazakh National University, 71, al-Farabi av., 050038, Almaty, Kazakhstan

DOI:

https://doi.org/10.18321/ectj287

Abstract

Activated carbons in this work were prepared from rice husk by phosphoric acid activation followed by alkaline desilication. Pseudo-random selection of 16 rice husk samples was subjected to carbonization at the
following conditions: 0.5 to 2 h of activation time, 300-600 ºС and Н3РО4/precursor (wt/wt) impregnation ratio of 0.5 to 2. Concentration of NaOH desilication solution varied from 0.5 to 2M. It was found that out of the four factors impregnation ratio is clearly the strongest and at the impregnation ratio of 2 for 1 h at 500 °C N2 BET-surface area reaches 1690 m2/g (SBET(Ar)=2492 m2/g) while pore volume becomes 1.95 cm3/g. Elemental analysis showed highest carbon content for this sample (87.96%). All samples have insignificant amount of Si and traces of metals, but considerable amount of phosphorus. Blocks of honeycomb structure prepared from Ca-montmorillonite and desilicated carbonized rice husk (impregnation ratio is 1.5, 1 h at 600 ºC) have BET-surface area obtained by thermal desorption of argon up to 856 m2/g.

References

1. Q. Feng, Q. Lin, F. Gong, S. Sugita, M. Shoya, J. Colloid Interf. Sci. 274 (2004) 1.

2. E. Natarajan, A. Nordin, A.N. Rao, Biomass Bioenergy 14 (1998) 533.

3. G. Doner and S. Akman, Fresen. Environ. Bull., 12 (7) (2003) 736.

4. P.K. Malik, Dyes and Pigments 56 (2003) 239.

5. Y. Guo, S. Yang, K. Yu, J. Zhao, Z. Wang, H.Xu, Materials Chemistry and Physics 74 (2002) 320.

6. Y. Guo, K. Yu, Z. Wang, H. Xu, Carbon 41 (2003) 1645.

7. N. Yalcin, A. Sevinc, Carbon 38 (2000) 1943.

8. A.A.M. Daifullah, B.S. Girgis, H.M.H. Gad, Colloids and Surfaces A: Physicochemical and Engineering Aspects 235 (2004) 1.

9. I.A. Rahman, B. Saad, B. Shaidan, E.S. Sya Rizal, BioresourceTechnology 96 (2005) 1578.

10. L.J. Kennedy, J.J. Vijaya, G. Sekaran, Industrial & Engineering Chemistry Research 43 (2004) 1832.

11. L.B. Khalil, Adsorption Science & Technology 14 (1996) 317.

12. S.A. Dastgheib, D.A. Rockstraw, Carbon 39 (2001) 1849.

13. C.A. Toles, W.E. Marshall, M.M. Johns, Carbon 37 (1999) 1207.

14. Y. Guo, D.A. Rockstraw / Microporous and Mesoporous Materials 100 (2007) 12–19.

15 Z.R. Ismagilov, N.V. Shikina, S.A. Yashnik, S.R. Khayrulin, V.N. Korotkikh, V.B. Koptenarmusov, A.A. Smislov and A.V. Polonik, Russian-Int. Conf. Catalytic Technologyes of Environments Protection for the Industry and Transport, St. Petersburg, 11-14 Dec. 2007, p.209.

16. Z.A. Mansurov, N.K. Zhylybaeva, P.S. Valieva, R.M. Mansurova, Chem. Sustainable Dev.10 (2002) 321.

17. M.M. Yemuranov, V.A. Biisenbayev, Z.A. Mansurov, A.N. Sabitov, Zh.M. Basygaeraev, S.A. Ibragimova, M.K. Gil’manov, Izvestiya NAS RK 3 (375) (2006) 76.

18. Z.A. Mansurov, in: R. Gross et al (Ed.), Nonoscale-Devices–Fundamentals and Ap plications, Springer, 2006,
p. 355.

19. Z.R. Ismagilov, Int. Seminar. Monolith Honeycomb Supports and Catalysts, St. Petersburg, 1995, p.9.

20. Ismagilov, Zinfer R., Shikina, Nadezhda V., Andrievskaya, Irina P., Rudina, Nina A., Mansurov, Zulkhair A., Burkitbaev, Mukash M.,. Preparation of carbonized rice husk monoliths and modification of the porous structure by SiO2 leaching. Catalysis Today, (2009), V.147, № 3-4, pp.58-65.

21. S.A. Yashnik, I.P. Andrievskaya, O.V. Pashke, Z.R. Ismagilov and J.A. Moulijn, Catalysis in Industry, 1 (2007) 35.

22. S.A. Yashnik, Z.R. Ismagilov, I.V. Koptyug, I.P.Andrievskaya, A.A.Matveev and J.A.Moulijn, Catal. Today, 105 (3-40 (2005) 507.

23. P.M. Yeletsky, V.A. Yakovlev, V.B. Fenelonov and V.N. Parmon, Kinet. Catal., 49 (2008) 708.

24. P.M. Yeletsky, V.A. Yakovlev, M.S. Mel’gunov and V.N. Parmon, Microporous Mesoporous Mater., 121 (2009) 34.

Downloads

Published

2009-09-20

How to Cite

Jandosov, J. M., Shikina, N. V., Bijsenbayev, M. A., Shamalov, M. E., Ismagilov, Z. R., & Mansurov, Z. A. (2009). Evaluation of Synthetic Conditions for H3PO4 Chemically Activated Rice Husk and Preparation of Honeycomb Monoliths. Eurasian Chemico-Technological Journal, 11(3), 245–252. https://doi.org/10.18321/ectj287

Issue

Section

Articles

Most read articles by the same author(s)

<< < 2 3 4 5 6 7 8 9 > >>