Charge and Discharge Behaviour of Li-Ion Batteries at Various Temperatures Containing LiCoO2 Nanostructured Cathode Produced by CCSO
DOI:
https://doi.org/10.18321/ectj235Abstract
There are technical barriers for penetration market requesting rechargeable lithium-ion battery packs for
portable devices that operate in extreme hot and cold environments. Many portable electronics are used in
very cold (-40 °C) environments, and many medical devices need batteries that operate at high temperatures.
Conventional Li-ion batteries start to suffer as the temperature drops below 0 °C and the internal impedance
of the battery increases. Battery capacity also reduced during the higher/lower temperatures. The present
work describes the laboratory made lithium ion battery behaviour features at different operation temperatures. The pouch-type battery was prepared by exploiting LiCoO2 cathode material synthesized by novel synthetic approach referred as Carbon Combustion Synthesis of Oxides (CCSO). The main goal of this paper focuses on evaluation of the efficiency of positive electrode produced by CCSO method. Performance studies of battery showed that the capacity fade of pouch type battery increases with increase in temperature. The experimental results demonstrate the dramatic effects on cell self-heating upon electrochemical performance. The study involves an extensive analysis of discharge and charge characteristics of battery at each temperature following 30 cycles. After 10 cycles, the battery cycled at RT and 45 °C showed, the capacity fade of 20% and 25% respectively. The discharge capacity for the battery cycled at 25 °C was found to be higher when compared with the battery cycled at 0 °C and 45 °C. The capacity of the battery also decreases when cycling at low temperatures. It was important time to charge the battery was only 2.5 hours to obtain identical nominal capacity under the charging protocol. The decrease capability of battery cycled at high temperature can be explained with secondary active material loss dominating the other losses.
References
2. Yan Ji, Yancheng Zhang, and Chao-Yang Wang, J. Electrochem. Soc. 160 (4) (2013) A636-A649.
3. D. Linden, Handbook of Batteries, McGrawHill, New York, (1995).
4. Y. Abu-Lebdeh, Nanotechnology for Li-ion batteries, Springer, (2013).
5. K.S. Martirosyan and D. Luss, AIChE J., 51 (10) (2005) 2801-2810.
6. K.S. Martirosyan and D. Luss, Carbon combustion synthesis of oxides, US Patent # 7,897,135, (2011).
7. A. Markov, I. Filimonov, and K.S. Martirosyan, J. of Computational Physics, 231 (2012) 6714-6724.
8. K.S. Martirosyan and D. Luss, Ind. Eng. Chem. Res., 46 (2007)1492-1499.
9. K.S. Martirosyan, M. Iliev, and D. Luss, Int. J. SHS, 16 (2007) 36-45.
10. K.S. Martirosyan, L. Chang, J. Rantschler, S. Khizroev, D. Luss and D. Litvinov, IEEE Transactions on Magnetics, 43 (6) (2007) 3118-3120.
11. A.G. Merzhanov, J. Mater. Chem. 14 (12) (2004) 1979-1791.
12. Y. Mamyrbaeva, M.A. Hobosyan, S.E. Kumekov, K.S. Martirosyan, Carbon Combustion Synthesis of Lithium Cobaltate, NSTI-NanoTech, 2 (2013) 657-659.
Downloads
Published
How to Cite
Issue
Section
License
You are free to: Share — copy and redistribute the material in any medium or format. Adapt — remix, transform, and build upon the material for any purpose, even commercially.
Eurasian Chemico-Technological Journal applies a Creative Commons Attribution 4.0 International License to articles and other works we publish.
Subject to the acceptance of the Article for publication in the Eurasian Chemico-Technological Journal, the Author(s) agrees to grant Eurasian Chemico-Technological Journal permission to publish the unpublished and original Article and all associated supplemental material under the Creative Commons Attribution 4.0 International license (CC BY 4.0).
Further distribution of this work must maintain attribution to the author(s) and the published article’s title, journal citation, and DOI.